Pressure blasting wet or dry black silicon carbide

Black silicon carbide is produced at high temperature in an electric resistance type furnace with quartz sand and petroleum coke as its main raw materials. Its hardness is between fused alumina and synthetic diamond. Mechanical intensity of it is higher than fused alumina. It is brittle and sharp and sharp and heat conductivity in some degree. The abrasive made of it are suitable for working on cast iron, non-ferrous metal, rock, leather, rubber, etc It is also broadly used as refractory material and metallurgical additive.

$1,500.00$1,560.00 / MT

Black silicon carbide is produced at high temperature in an electric resistance type furnace with quartz sand and petroleum coke as its main raw materials. Its hardness is between fused alumina and synthetic diamond. Mechanical intensity of it is higher than fused alumina. It is brittle and sharp and sharp and heat conductivity in some degree. The abrasive made of it are suitable for working on cast iron, non-ferrous metal, rock, leather, rubber, etc It is also broadly used as refractory material and metallurgical additive.

TYPICAL CHEMICAL ANALYSIS
TYPICAL PHISICAL PROPERTIES
SiC
≥98%
Hardness:
Mohs:9.2
SiO2
≤1%
Melting Point:
Sublimes at 2250 ℃
H2O3
≤0.5%
Maximum service temperature:
1900℃
Fe2O3
≤0.3%
Specific Gravity:
3.2-3.45 g/cm3
F.C
≤0.3%
Bulk density(LPD):
1.2-1.6 g/cm3
Magnetic content
≤0.02%
Color:
Black
Particle shape:
Hexagonal
Available Sizes
P-microgrits
P240 P280 P320 P360 P400 P500 P600 P800 P1000 P1200 P1500 P2000 P2500 P3000 P4000 P5000
FEPA
F230 F240 F280 F320 F360 F400 F500 F600 F800 F1000 F1200 F1500 F2000
JIS
240# 280# 320# 360# 400# 500# 600# 700# 800# 1000# 1200# 1500# 2000# 2500# 3000# 4000# 6000#8000#

Weight1000 kg
Dimensions100 × 100 × 100 cm

Reviews

There are no reviews yet.

Be the first to review “Pressure blasting wet or dry black silicon carbide”

Your email address will not be published. Required fields are marked *

PDF-LOGO-100-.png

TDS not uploaded

PDF-LOGO-100-.png

MSDS not uploaded

Please enter correct URL of your document.

Scroll to Top